SABIC Innovative Plastics NORYL GTX GTX989 PPE+PA (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	NORYL GTX
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL GTX GTX989 PPE+PA (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

NORYL GTX989 is a conductive and high heat material, especially designed for in- and on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static painting in an unique way.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D792
Density	1.08 g/cc	0.0390 lb/inÂ³	ISO 1183
Moisture Absorption	1.20 %	1.20 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	4.2 %	4.2 %	ISO 62
Linear Mold Shrinkage, Flow	0.012 - 0.016 cm/cm @Thickness 3.20 mm	0.012 - 0.016 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	16 g/10 min @Load 5.00 kg, Temperature 280 Â°C	16 g/10 min @Load 11.0 lb, Temperature 536 Â°F	ASTM D1238
Melt Index of Compound	19 g/10 min @Load 5.00 kg, Temperature 280 Â°C	19 g/10 min @Load 11.0 lb, Temperature 536 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	50 mm/min; ISO 527
	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ISO 527
	65.0 MPa	9430 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	40 %	40 %	50 mm/min; ISO 527
	45 %	45 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D638
	5.0 %	5.0 %	50 mm/min; ISO 527
Tensile Modulus	2.30 GPa	334 ksi	1 mm/min; ISO 527
	2.35 GPa	341 ksi	50 mm/min; ASTM D638
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
	95.0 MPa	13800 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.30 GPa	334 ksi	2 mm/min; ISO 178
	2.45 GPa	355 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	2.40 J/cm	4.50 ft-lb/in	ASTM D256
	1.80 J/cm @Temperature -30.0 Â°C	3.37 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Notched (ISO)	22.0 kJ/mÂ²	10.5 ft-lb/inÂ²	80104; ISO 180/1A
	15.0 kJ/mÂ² @Temperature -30.0 Â°C	7.14 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	2.20 J/cmÂ²	10.5 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
	1.50 J/cmÂ² @Temperature -30.0 Â°C	7.14 ft-lb/inÂ² @Temperature -22.0 Â°F	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	60.0 J @Temperature 23.0 Â°C	44.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	85.0 Âµm/m-Â°C @Temperature -40.0 - 60.0 Â°C	47.2 Âµin/in-Â°F @Temperature -40.0 - 140 Â°F	ASTM E 831
	90.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	50.0 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	85.0 Âµm/m-Â°C @Temperature -40.0 - 60.0 Â°C	47.2 Âµin/in-Â°F @Temperature -40.0 - 140 Â°F	ASTM E 831
	90.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	50.0 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	185 Â°C	365 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
	190 Â°C @Thickness 3.20 mm	374 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	180 Â°C	356 Â°F	Rate B/50; ASTM D1525
	195 Â°C	383 Â°F	Rate B/50; ISO 306
	198 Â°C	388 Â°F	Rate B/120; ISO 306

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 - 10000 ohm-cm	1000 - 10000 ohm-cm	SABIC Method