SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 1.20 %
1.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 4.2 %
4.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.014 - 0.017 cm/cm

@Thickness 3.20 mm
0.014 - 0.017 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm

@Thickness 3.20 mm
0.012 - 0.015 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 280 °C
20 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 280 °C
12 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 30 %
30 %
50 mm/min; ISO 527
55 %
55 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
50 mm/min; ASTM D638
2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
1.3 mm/min, 50 mm span; ASTM D790
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.30 J/cm
2.44 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
1.50 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
195 °C

@Thickness 3.20 mm
383 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 195 °C
383 °F
Rate B/50; ISO 306
200 °C
392 °F
Rate B/120; ISO 306
200 °C
392 °F
Rate B/50; ASTM D1525
Electrical Properties Metric English Comments
Volume Resistivity 1000 - 10000 ohm-cm
1000 - 10000 ohm-cm
SABIC Method
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2