DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® 103FHS BKB038 is a heat stabilized, lubricated, PA 66 resin for fast cycling.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Thickness 2.00 mm
0.014 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Thickness 2.00 mm
0.013 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.0 MPa

@Temperature 23.0 °C
12300 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 18 %

@Temperature 23.0 °C
18 %

@Temperature 73.4 °F
DAM; nominal; ISO 527
Elongation at Yield 4.5 %

@Temperature 23.0 °C
4.5 %

@Temperature 73.4 °F
DAM; ISO 527
Tensile Modulus 3.10 GPa

@Temperature 23.0 °C
450 ksi

@Temperature 73.4 °F
DAM; ISO 527
Flexural Modulus 2.80 GPa

@Temperature 23.0 °C
406 ksi

@Temperature 73.4 °F
DAM; ISO 178
Izod Impact, Notched (ISO) 5.50 kJ/m²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 300 kJ/m²

@Temperature 23.0 °C
143 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
DAM; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
DAM; ISO 75-1/-2
Glow Wire Test 725 °C

@Thickness 1.50 mm
1340 °F

@Thickness 0.0591 in
DAM; Ignition; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
1340 °F

@Thickness 0.118 in
DAM; Ignition; IEC 60695-2-13
725 °C

@Thickness 0.710 mm
1340 °F

@Thickness 0.0280 in
DAM; Ignition; IEC 60695-2-13
850 °C

@Thickness 0.710 mm
1560 °F

@Thickness 0.0280 in
DAM; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
DAM; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
DAM; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
DAM; Optimum
280 - 300 °C
536 - 572 °F
DAM
Mold Temperature 70.0 °C
158 °F
DAM; optimum
50.0 - 90.0 °C
122 - 194 °F
DAM
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Forms Pellets
DAM
Generic Nylon 66
DAM
Material Status Current
DAM
Processing Method Injection Molding
DAM
Product Category Unreinforced Resins
DAM
RoHS Compliance Contact Manufacturer
DAM