Overview of materials for Polycarbonate, Glass Fiber Filled, Flame Retardant

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate, Glass Fiber Filled, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 1.63 g/cc
0.0434 - 0.0589 lb/in³
Average value: 1.34 g/cc Grade Count:121
Filler Content 5.00 - 40.0 %
5.00 - 40.0 %
Average value: 21.0 % Grade Count:36
Water Absorption 0.0600 - 0.350 %
0.0600 - 0.350 %
Average value: 0.116 % Grade Count:52
Moisture Absorption at Equilibrium 0.100 - 0.250 %
0.100 - 0.250 %
Average value: 0.200 % Grade Count:5
Water Absorption at Saturation 0.120 - 0.350 %
0.120 - 0.350 %
Average value: 0.210 % Grade Count:5
Additive Loading 10.0 - 30.0 %
10.0 - 30.0 %
Average value: 17.5 % Grade Count:8
Linear Mold Shrinkage 0.000200 - 0.00900 cm/cm
0.000200 - 0.00900 in/in
Average value: 0.00341 cm/cm Grade Count:110
Linear Mold Shrinkage, Transverse 0.00200 - 0.00750 cm/cm
0.00200 - 0.00750 in/in
Average value: 0.00442 cm/cm Grade Count:15
Melt Flow 3.00 - 17.0 g/10 min
3.00 - 17.0 g/10 min
Average value: 10.1 g/10 min Grade Count:36
Mechanical Properties Metric English Comments
Hardness, Rockwell M 83.0 - 95.0
83.0 - 95.0
Average value: 85.7 Grade Count:9
Hardness, Rockwell R 118 - 124
118 - 124
Average value: 120 Grade Count:43
Tensile Strength, Ultimate 45.0 - 172 MPa
6530 - 24900 psi
Average value: 84.3 MPa Grade Count:94
25.0 - 85.0 MPa

@Temperature 60.0 - 120 °C
3630 - 12300 psi

@Temperature 140 - 248 °F
Average value: 60.0 MPa Grade Count:2
Tensile Strength, Yield 55.8 - 172 MPa
8100 - 24900 psi
Average value: 79.1 MPa Grade Count:46
Elongation at Break 1.00 - 100 %
1.00 - 100 %
Average value: 8.18 % Grade Count:102
1.50 - 28.0 %

@Temperature 60.0 - 120 °C
1.50 - 28.0 %

@Temperature 140 - 248 °F
Average value: 38.8 % Grade Count:2
Elongation at Yield 4.00 - 8.00 %
4.00 - 8.00 %
Average value: 5.44 % Grade Count:9
2.20 - 3.00 %

@Temperature 60.0 - 120 °C
2.20 - 3.00 %

@Temperature 140 - 248 °F
Average value: 2.67 % Grade Count:1
Modulus of Elasticity 2.20 - 16.5 GPa
319 - 2390 ksi
Average value: 5.74 GPa Grade Count:64
2.20 - 6.00 GPa

@Temperature 60.0 - 120 °C
319 - 870 ksi

@Temperature 140 - 248 °F
Average value: 4.02 GPa Grade Count:2
Flexural Yield Strength 75.8 - 262 MPa
11000 - 38000 psi
Average value: 134 MPa Grade Count:100
Flexural Modulus 2.40 - 12.4 GPa
348 - 1800 ksi
Average value: 4.96 GPa Grade Count:115
Compressive Yield Strength 96.5 - 148 MPa
14000 - 21500 psi
Average value: 114 MPa Grade Count:3
Izod Impact, Notched 0.427 - 8.00 J/cm
0.800 - 15.0 ft-lb/in
Average value: 1.34 J/cm Grade Count:102
1.00 - 1.00 J/cm

@Temperature 0.000 - 0.000 °C
1.87 - 1.87 ft-lb/in

@Temperature 32.0 - 32.0 °F
Average value: 0.960 J/cm Grade Count:2
0.900 - 1.08 J/cm

@Temperature -30.0 - -30.0 °C
1.69 - 2.02 ft-lb/in

@Temperature -22.0 - -22.0 °F
Average value: 0.960 J/cm Grade Count:4
0.900 - 1.08 J/cm

@Thickness 3.20 - 3.20 mm
1.69 - 2.02 ft-lb/in

@Thickness 0.126 - 0.126 in
Average value: 0.960 J/cm Grade Count:4
Izod Impact, Unnotched 0.400 J/cm - NB
0.749 ft-lb/in - NB
Average value: 8.97 J/cm Grade Count:44
Izod Impact, Notched (ISO) 8.00 - 11.0 kJ/m²
3.81 - 5.23 ft-lb/in²
Average value: 9.20 kJ/m² Grade Count:5
8.00 - 8.00 kJ/m²

@Temperature -30.0 - -30.0 °C
3.81 - 3.81 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 8.00 kJ/m² Grade Count:1
Charpy Impact Unnotched 3.50 - 1000 J/cm²
16.7 - 4760 ft-lb/in²
Average value: 4.50 J/cm² Grade Count:7
0.800 - 999.9 J/cm²

@Temperature -30.0 - -20.0 °C
3.81 - 4759 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.800 J/cm² Grade Count:2
Charpy Impact, Notched 0.700 - 1.20 J/cm²
3.33 - 5.71 ft-lb/in²
Average value: 0.850 J/cm² Grade Count:13
0.600 - 0.700 J/cm²

@Temperature -20.0 - -20.0 °C
2.86 - 3.33 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.629 J/cm² Grade Count:7
Tensile Impact Strength 53.3 - 147 kJ/m²
25.4 - 69.9 ft-lb/in²
Average value: 100 kJ/m² Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 20.0 - 40.0 µm/m-°C
11.1 - 22.2 µin/in-°F
Average value: 30.5 µm/m-°C Grade Count:15
CTE, linear, Transverse to Flow 60.0 - 65.0 µm/m-°C
33.3 - 36.1 µin/in-°F
Average value: 60.8 µm/m-°C Grade Count:6
Thermal Conductivity 0.216 - 0.350 W/m-K
1.50 - 2.43 BTU-in/hr-ft²-°F
Average value: 0.294 W/m-K Grade Count:3
Hot Ball Pressure Test 135 °C
275 °F
Average value: 135 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 130 - 265 °C
266 - 509 °F
Average value: 147 °C Grade Count:91
Deflection Temperature at 1.8 MPa (264 psi) 104 - 207 °C
220 - 405 °F
Average value: 140 °C Grade Count:101
Vicat Softening Point 140 - 186 °C
284 - 367 °F
Average value: 151 °C Grade Count:26
Heat Distortion Temperature 140 - 146 °C
284 - 295 °F
Average value: 144 °C Grade Count:4
UL RTI, Electrical 80.0 - 130 °C
176 - 266 °F
Average value: 102 °C Grade Count:13
Electrical Properties Metric English Comments
Electrical Resistivity 1e+05 - 1.00e+16 ohm-cm
1e+05 - 1.00e+16 ohm-cm
Average value: 8.27e+15 ohm-cm Grade Count:53
Surface Resistance 1.00e+9 - 1.00e+16 ohm
1.00e+9 - 1.00e+16 ohm
Average value: 2.84e+15 ohm Grade Count:19
Static Decay 2.00 sec
2.00 sec
Average value: 2.00 sec Grade Count:4
Dielectric Constant 3.00 - 3.80
3.00 - 3.80
Average value: 3.30 Grade Count:27
Dielectric Strength 17.0 - 38.0 kV/mm
432 - 965 kV/in
Average value: 22.2 kV/mm Grade Count:38
Dissipation Factor 0.000800 - 0.0200
0.000800 - 0.0200
Average value: 0.00650 Grade Count:26
Arc Resistance 0.000 - 120 sec
0.000 - 120 sec
Average value: 96.5 sec Grade Count:15
Comparative Tracking Index 100 - 250 V
100 - 250 V
Average value: 182 V Grade Count:15
Hot Wire Ignition, HWI 30.0 - 120 sec
30.0 - 120 sec
Average value: 76.3 sec Grade Count:7
High Amp Arc Ignition, HAI 15.0 - 120 arcs
15.0 - 120 arcs
Average value: 99.4 arcs Grade Count:7
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Average value: 115 mm/min Grade Count:4