SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX914 is an unfilled GTX grade with an ideal combination of impact performance, dimensional stability at elevated temperatures, chemical resistance and processability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.5 % | 3.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | on Tensile Bar; SABIC Method |
| 0.013 - 0.016 cm/cm @Thickness 3.20 mm |
0.013 - 0.016 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.014 cm/cm @Thickness 3.20 mm |
0.011 - 0.014 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 280 °C |
12 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min @Load 5.00 kg, Temperature 280 °C |
11 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ISO 527 |
| 100 % | 100 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 7.5 % | 7.5 % | 50 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.95 GPa | 283 ksi | 50 mm/min; ASTM D638 |
| 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.80 J/cm | 5.25 ft-lb/in | ASTM D256 |
| 1.20 J/cm @Temperature -30.0 °C |
2.25 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/2C | |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 190 °C | 374 °F | Rate B/50; ISO 306 |
| 195 °C | 383 °F | Rate B/120; ISO 306 | |
| 195 °C | 383 °F | Rate B/50; ASTM D1525 | |
| 245 °C | 473 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.5 @Frequency 50.0 - 60.0 Hz |
3.5 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.072 @Frequency 50.0 - 60.0 Hz |
0.072 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Saint-Gobain Norton® UHMW PE Skived PTFE Film
- Teknor Apex APEX® RE 8003 Polyvinyl Chloride, Rigid
- Teknor Apex ELEXAR® EL 8451 Thermoplastic Elastomer
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >0.500-1.000 in, STD, Per Mil-T-9047G
- Wanhua Chemical Wanthane® WHT-2185 Polycaprolactone Based TPU
- EPICHEM Epilon G2-PC 10% GF Polycarbonate, 10% Glass Fiber
- A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified
- 3M Scotch-Weld™ GM10 Gasket Maker Anaerobic Adhesive
- Fainplast Compounds PH 58/AL Flexible PVC, Transparent Extrusion
- Industeel CLC 18.9 L General Purpose 18Cr-9Ni Austenitic Stainless Steel
Copyright © lookpolymers.com All Rights Reserved