SABIC Innovative Plastics Geloy XTWM200 ASA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy XTWM200 ASA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ASA resin for injection molding. Excellent flow, colorability and outdoor weathering capability.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D 792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.55 %

@Temperature 23.0 °C
 0.55 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 12 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 12 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
13.3 g/10 min

@Load 3.80 kg,
Temperature 280 °C
 13.3 g/10 min

@Load 8.38 lb,
Temperature 536 °F
 ASTM D 1238
15 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 15 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D 1238
18 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 18 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 103
103
ASTM D 785
Tensile Strength at Break 34.0 MPa
4930 psi
50 mm/min; ISO 527
35.0 MPa
5080 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 20 %
20 %
Type I, 50 mm/min; ASTM D 638
28 %
28 %
50 mm/min; ISO 527
Elongation at Yield 2.8 %
2.8 %
Type I, 50 mm/min; ASTM D 638
2.8 %
2.8 %
50 mm/min; ISO 527
Tensile Modulus 2.39 GPa
347 ksi
5 mm/min; ASTM D 638
2.52 GPa
365 ksi
50 mm/min; ASTM D 638
2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 72.0 MPa
10400 psi
2 mm/min; ISO 178
75.0 MPa
10900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.45 GPa
355 ksi
2 mm/min; ISO 178
2.57 GPa
373 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.240 J/cm

@Temperature -30.0 °C
 0.450 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
0.650 J/cm

@Temperature 23.0 °C
 1.22 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 3.00 J

@Temperature -30.0 °C
 2.21 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Total Energy; ASTM D 3763
40.0 J

@Temperature 23.0 °C
 29.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
88.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
86.0 °C

@Thickness 3.20 mm
 187 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
77.0 °C

@Thickness 3.20 mm
 171 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 88.0 °C
190 °F
Rate B/50; ISO 306
93.0 °C
199 °F
Rate B/120; ISO 306
95.0 °C
203 °F
Rate B/50; ASTM D 1525
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94
Optical Properties Metric English Comments
Gloss 94 %
94 %
untextured, 60 degrees; ASTM D 523
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C NA
IEC 60695-10-2
UV-light, water exposure/immersion F1
UL 746C