Victrex® PEEK 450P Polyetheretherketone, Unreinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 450P Polyetheretherketone, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, coarse powder for extrusion compounding, standard flow, FDA food contact compliant, colour natural.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Viscosity 350000 cP

@Temperature 400 °C
350000 cP

@Temperature 752 °F
ISO 11443
Mechanical Properties Metric English Comments
Tensile Strength, Yield 98.0 MPa

@Temperature 23.0 °C
14200 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 30 %

@Temperature 23.0 °C
30 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 4.00 GPa

@Temperature 23.0 °C
580 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 160 MPa

@Temperature 23.0 °C
23200 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 3.80 GPa

@Temperature 23.0 °C
551 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/U
Thermal Properties Metric English Comments
Melting Point 343 °C
649 °F
ISO 11357
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
150 °C
302 °F
Midpoint; ISO 11357
Processing Properties Metric English Comments
Processing Temperature 380 - 400 °C
716 - 752 °F
Dry Time 3.00 hour

@Temperature 150 °C
3.00 hour

@Temperature 302 °F
5.00 hour

@Temperature 120 °C
5.00 hour

@Temperature 248 °F