SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. GTX679 has improved impact/elongation and the mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.6 % | 3.6 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 220 °C |
14 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.45 GPa | 645 ksi | 5 mm/min; ASTM D638 |
| 4.79 GPa | 695 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 109 MPa | 15800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.44 GPa | 644 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| 0.310 J/cm @Temperature -30.0 °C |
0.581 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 59.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 64.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 185 °C @Thickness 3.20 mm |
365 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 185 °C | 365 °F | Rate B/50; ASTM D1525 |
| 185 °C | 365 °F | Rate B/50; ISO 306 | |
| 188 °C | 370 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NYCOA 436 PA 6
- PolyOne Geon™ Vinyl Wire & Cable 3701-xx01D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymax® Maxelast® P2770 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics LNP LUBRICOMP RX05496 PA 66
- SABIC Innovative Plastics ULTEM LTX300B PEI
- Silberline Silvex® 440-15-C
- CPC - Vycom Corzan® CPVC Chlorinated PVC
- ChevronTexaco Quenchtex® MM
- Beijing Ranger Chem SM-634X90 Solvent Based Epoxy Resin
- SABIC Innovative Plastics NORYL GTX GTX6203 PPE+PA (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved