SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* D451 (or EXTC8141) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm @Time 86400 sec |
0.0010 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0025 cm/cm @Time 86400 sec |
0.0010 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 17.9 g/10 min @Load 2.16 kg, Temperature 300 °C |
17.9 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D1238 |
| 57 g/10 min @Load 5.00 kg, Temperature 300 °C |
57 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 300 °C |
14 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 42 g/10 min @Load 5.00 kg, Temperature 300 °C |
42 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 143 MPa | 20700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 11.72 GPa | 1700 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.75 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.21 J/cm | 9.76 ft-lb/in | ASTM D4812 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C @Thickness 3.20 mm |
237 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FS-1602 Silicon Iron Soft Magnetic Powdered Metal
- Resin Technology Group Fusion 519 Wicking Grade Fusion Cyanoacrylate
- Kennametal Stellite Stellite® 33
- Freudenberg Simrit V178 Non-Black Compound
- MRC Polymers MAXTELâ„¢ 600 GF20 TPO, 20% Glass Fiber Filled
- Solvay Specialty Polymers Kalix® 3850 Polyamide, High Performance (HPPA), 50% Glass Fiber
- SABIC Innovative Plastics LNP Stat-kon OCL13 PPS - LINEAR (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP VERTON MX02795 PP (Asia Pacific)
- A. Schulman POLYFORT™ PP 1329 Medium Impact Copolymer Polypropylene
- Aaron Industries AAROLENE® ARPE LD 300-1 Low Density Polyethylene Compounded Resin
Copyright © lookpolymers.com All Rights Reserved