Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Chemical test |
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | melt index; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min; parallel to flow; ASTM D638 |
| Elongation at Break | 70 % | 70 % | 5 mm/min; parallel to flow; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 13 | 13 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 210 °C | 374 - 410 °F | Cylinder temp |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 89.0 - 90.0 °C | 192 - 194 °F | Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice. |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- Prodways PLASTCure Flex 100 3D Printing Polymer
- A. Schulman CP812 Linear, Medium-Density Polyethylene
- Dow Corning 748 NON-CORROSIVE SEALANT
- ConocoPhillips Tacna® 2000 NLGI No. 2
- Eastman Eastman AP006 Copolyester
- Ensinger Tecapeek® GF30 Polyetheretherketone, 30% Glass Reinforced (PEEK)
- Epoxy Technology EPO-TEK® 377 High Temperature Epoxy
- ConocoPhillips Conoflex® 32 SRI Lubricant ISO
- Bayshore Vinyl Compounds BRC R7550 CLR 223V Extrusion Compound
- Chem Polymer Chemlon 206 G Nylon 6, 6% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved