SABIC Innovative Plastics NORYL GFN1 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN1 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 10% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16.6 g/10 min @Load 5.00 kg, Temperature 300 °C |
16.6 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 300 °C |
16 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Tensile Modulus | 4.35 GPa | 631 ksi | 5 mm/min; ASTM D638 |
| 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 122 MPa | 17700 psi | ISO 178 |
| Flexural Yield Strength | 107 MPa | 15500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 116 MPa | 16800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.58 GPa | 519 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 3.84 GPa | 557 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 4.16 GPa | 603 ksi | ISO 178 | |
| Izod Impact, Notched | 1.18 J/cm | 2.21 ft-lb/in | ASTM D256 |
| 1.03 J/cm @Temperature -30.0 °C |
1.93 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.49 J/cm | 8.41 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.40 J/cm² | 16.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.30 J/cm² @Temperature -30.0 °C |
15.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/2C |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 71.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 131 °C | 268 °F | Rate B/50; ISO 306 |
| 134 °C | 273 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 90.0 °C | 194 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0014 @Frequency 1.00e+6 Hz |
0.0014 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Hot Wire Ignition, HWI | 0.00 - 7.0 sec | 0.00 - 7.0 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Nyco MG WOLLASTOCOAT® Wollastonite
- PolyOne Nymax™ GF 1200 A 33 Natural Polyamide 66 (Nylon 66)
- DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation (discontinued **)
- SABIC Innovative Plastics ULTEM Foam XP080 PEI (Asia Pacific)
- Shakespeare WP-315 diameter 0.2 mm Weft Polyester Monofilament
- Trelleborg AEM Eccofloat® EL-36/7300 Syntactic Foam
- Ecomass® 1080ZD93 Tungsten Powder Filled Polyamide Alloy, Injection Molding Grade
- Chosun Refractories TAST-160 Monolithic Refractories for Ladle and Tundish
- Alliance Polymers Zythane™ 4050D Thermoplastic Polyurethane Elastomer
- LATI Latilub 88/50-30GRT PEEK, Graphite/PTFE Filled
Copyright © lookpolymers.com All Rights Reserved