Ineos Nova 5400 High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 5400 High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | Condition G |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 40 | 40 | |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Modulus of Elasticity | 1.897 GPa | 275.1 ksi | ASTM D638 |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.069 GPa | 300.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Diameter 3.17 mm |
2.60 ft-lb/in @Diameter 0.125 in |
bar, 0.010" notch radius; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.59 @Frequency 1e+6 Hz |
2.59 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 15.7 kV/mm @Thickness 3.17 mm |
400 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ FSL 7586/40 Fluorinated Liquid Silicone Rubber
- Karina 790-38/23-CRPC Straw CPVC Compound
- Techmer ES HiFill® PA6/6 L N MB Nylon 66
- Alcoa QC-10® Aluminum Mold Alloy
- Dow Corning SILASTIC® 25787 SILICONE RUBBER NATURAL
- Alliance Polymers Viprene™ P80A-22U-NAT Thermoplastic Vulcanizate Elastomer
- Petroquimica Triunfo Trithene® SX 9003 MDPE - Blow Molding
- DuPont Performance Polymers Zytel® HTN 92G35DH2 BK083 Polyphthalamide (PPA) (Unverified Data**)
- Potters Industries Q-Cel® 6014
Copyright © lookpolymers.com All Rights Reserved