Dow 650I Low Density Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow 650I Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW LDPE 650I Resin is intended for use in soft goods over wrap, bread bags, shrink films and other general purpose applications.Information provided by Dow
Physical Properties Metric English Comments
Density 0.928 g/cc
0.0335 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.58 MPa
2115 psi
ASTM D882
Film Tensile Strength at Yield, TD 14.60 MPa
2118 psi
ASTM D882
Film Elongation at Break, MD 606 %
606 %
ASTM D882
Film Elongation at Break, TD 780 %
780 %
ASTM D882
Secant Modulus, MD 0.2470 GPa
35.82 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.2751 GPa
39.90 ksi
2% Secant; ASTM D882
Impact 32
32
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
2532
2532
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
2640
2640
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Elmendorf Tear Strength MD 379 g
379 g
ASTM D1922
Elmendorf Tear Strength TD 449 g
449 g
ASTM D1922
Elmendorf Tear Strength, MD 7.461 g/micron
189.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 8.839 g/micron
224.5 g/mil
ASTM D1922
Dart Drop Test 89.0 g
0.196 lb
Method A; ASTM D1709
Film Tensile Strength at Break, MD 24.24 MPa
3515 psi
ASTM D882
Film Tensile Strength at Break, TD 21.04 MPa
3051 psi
ASTM D882
Optical Properties Metric English Comments
Haze 7.2 %
7.2 %
ASTM D1003
Gloss 77 %
77 %
45°; ASTM D2457