SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Commercial grade for Polycarbonate in only nature color. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D 792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.28 % @Temperature 23.0 °C |
0.28 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 2.30 - 4.60 mm |
0.0060 - 0.0080 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D 1238 |
| 43 g/10 min @Load 1.20 kg, Temperature 300 °C |
43 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 45 g/10 min @Load 1.20 kg, Temperature 300 °C |
45 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
| 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
| 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D 638 |
| 70 % | 70 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.65 GPa | 384 ksi | 1 mm/min; ISO 527 |
| 2.67 GPa | 387 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 105 MPa | 15200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm @Temperature -30.0 °C |
0.693 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.400 J/cm @Temperature 23.0 °C |
0.749 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 181 kJ/m² @Temperature -30.0 °C |
86.1 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| 182 kJ/m² @Temperature 23.0 °C |
86.6 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 13.0 J/cm² @Temperature -30.0 °C |
61.9 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 13.1 J/cm² @Temperature 23.0 °C |
62.3 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
41.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 111 °C | 232 °F | Rate B/50; ISO 306 |
| 114 °C | 237 °F | Rate B/120; ISO 306 | |
| 114 °C | 237 °F | Rate B/50; ASTM D 1525 | |
| Flammability, UL94 | V-1 @Thickness 2.00 mm |
V-1 @Thickness 0.0787 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Perstorp Compounds AMITEC VXO UF/MF blend
- Permabond UV630 UV-curable Adhesive
- H.C. Starck Amperit® 512.059 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- LyondellBasell Hifaxâ„¢ ETA-3081 Thermoplastic Olefin Resin
- Haynes Hastelloy® C-276 alloy, solution heat treated flat products
- Covestro Apec® HT KU 1-9341 High-Heat Polycarbonate
- Chosun Refractories TCH-175S Torpedo Castable
- Overview of materials for Medium Density Polyethylene (MDPE), Rotational Molded
Copyright © lookpolymers.com All Rights Reserved