Arlon R37881R015 Silicone Rubber/Fiberglass
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R37881R015 Silicone Rubber/Fiberglass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 1.5 mil PE; Side 1: uncured silicone rubber; Substrate: 1528 fiberglass; Side 2: uncured silicone rubber; Interleave: 1.5 mil PE
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 102 microns | 4.00 mil | side 1; Arlon SQA-TMS-003 |
| 102 microns | 4.00 mil | side 2; Arlon SQA-TMS-003 | |
| 178 microns | 7.00 mil | substrate; Arlon SQA-TMS-003 | |
| 381 microns | 15.0 mil | overall; Arlon SQA-TMS-003 | |
| Outgassing - Total Mass Loss | 0.34 % | 0.34 % | post cure; ASTM E 595 |
| 1.07 % | 1.07 % | no post cure; ASTM E 595 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 48 | 48 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 5.86 MPa | 850 psi | silicone property; ASTM D412 |
| Elongation at Break | 450 % | 450 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0621 MPa | 9.00 psi | Arlon SQA-TMS-011 |
| Tear Strength | 12.3 kN/m | 70.0 pli | Die B; silicone property; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 218 °C |
2.00 hour @Temperature 425 °F |
|
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
||
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Outgassing - CVCM (%) ASTM E595 | 0.1 | post cure |
| 0.28 | no post cure |
Users viewing this material also viewed the following:
- Ovation Polymers RIGITRON 30525 GF FR PET, 25% Glass Reinforced
- Kazanorgsintez M 115 Polymer Composition for Rotary Molding
- LG Chemical Lupox® DP1000DU PBT
- Lubriplate TEMP LOW Anhydrous Calcium Multi-Purpose Grease For Special Conditions
- SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly (Asia Pacific)
- Plenco 6553 Phenolic, Granular, Compression Molded
- Covestro Bayblend® T88 GF-30 Rubber Modified PC Blend, 31% Glass Filled
- Colorite Polymers 6511G-015 (Extrustion), 6512G-015 (Molding) Radiation Sterilizable Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved