SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UFL36AS is a Polyphthalamide (PPA) base resin containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 |
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 189 MPa | 27400 psi | Type I, 5 mm/min; ASTM D638 |
| 192 MPa | 27800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 189 MPa | 27400 psi | Type I, 5 mm/min; ASTM D638 |
| 192 MPa | 27800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.57 GPa | 1823 ksi | 1 mm/min; ISO 527 |
| 15.42 GPa | 2236 ksi | 50 mm/min; ASTM D638 | |
| 15.42 GPa | 2236 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 242 MPa | 35100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.29 GPa | 1637 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.950 J/cm | 1.78 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.09 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 273 °C | 523 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalen 3P-M3520B Polypropylene, 20% EPDM Filled
- Ineos Nova 1531 High Heat Crystal Polystyrene (discontinued **)
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
- Solvay Specialty Polymers Meforex® 32 Ozone-Friendly CFC Replacement
- Goodfellow Carbon/Epoxy Composite Sheet
- BASF Elastollan® C-70AW Polyester Type Polyurethane Elastomer
- Sinotek Materials Soft Graphite Ring
Copyright © lookpolymers.com All Rights Reserved