SABIC Innovative Plastics Lexan® FXD171R PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXD171R PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent/transluscent PC for light diffusion special effects. MFR of 25.0.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 125 % | 125 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 6.2 % | 6.2 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.33 GPa | 338 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 7.79 J/cm @Temperature 23.0 °C |
14.6 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Impact Test | 70.0 J @Temperature 23.0 °C |
51.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.09 mm |
V-2 @Thickness 0.0429 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | transparent/translucent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC code 2; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | surface, PLC code 1; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
Users viewing this material also viewed the following:
- Proto3000 Accura® 50 Plastic Stereolithography (SLA) Prototyping Polymer
- Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
- Lanxess Pocan® S 1506 000000 PBT
- Techmer ES Elastoblend® PA6/6 GF14 IM L 14% Glass Filled
- Styrolution Styrolux T SBC
- Solvay GEROPON® HW 25 N Surfactant
- Techmer ES Elastoblend® PA6/66 IM3 BK
- DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge
- 3M 5491 PTFE Extruded Film Tape
- Ashley Polymers Ashlene® 980LS-33G Nylon 612, 33% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved