Arlon 0.020" (0.508 mm) Silicone Traction Motor Insulation with Fiberglass Substrate (19220R020)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Silicone
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 0.020" (0.508 mm) Silicone Traction Motor Insulation with Fiberglass Substrate (19220R020).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Uncured silicone rubber with a minimum thickness of 0.005 in. (0.13 mm) on Prime Coated 1523 Fiberglass; 0.0015 in. (0.8 mm) polyethylene interleave; overall thickness 0.020 in ± 0.0015 (0.51 mm ± 0.038). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 759.5 g/m² ± 50.9 (22.4 oz./yd.² ± 1.5). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours. Maximum Flame and Glow Time: 15 seconds. Maximum Char Length: 7.6 cm (3 in). Bond strength is 8.2 kg/cm (9.5 lb/in.).Information provided by the manufacturer, Arlon Silicone Technologies Division.
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Tensile Strength, Ultimate >= 6.90 MPa
>= 1000 psi
Elongation at Break 250 %
250 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.6 °C
-69.9 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.75 kV/mm
>= 400.0 kV/in
Processing Properties Metric English Comments
Processing Temperature 176.6 °C
349.9 °F
curing temp., at 0.345 MPa (50 psi)