SABIC Innovative Plastics Lexan® FL920 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FL920 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Various weight reductions at .250"" (6.35 mm) wall, 20% GR. Excellent flex mod, high tensile strength/heat resistance. V-0/5V at .250"" (6.35mm).
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
foam molded; ASTM D792
1.32 g/cc
1.32 g/cc
ASTM D792
Water Absorption 0.14 %

@Time 86400 sec
 0.14 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.30 %
0.30 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 6.40 mm
 0.0030 - 0.0050 in/in

@Thickness 0.252 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.0 MPa

@Thickness 6.35 mm
 8410 psi

@Thickness 0.250 in
 ASTM D638
Elongation at Break 3.6 %

@Thickness 6.35 mm
 3.6 %

@Thickness 0.250 in
 ASTM D638
Tensile Modulus 4.27 GPa

@Thickness 6.40 mm
 619 ksi

@Thickness 0.252 in
 ASTM D638
Flexural Yield Strength 106 MPa
15400 psi
6.4 mm; ASTM D790
Flexural Modulus 5.13 GPa
744 ksi
6.4 mm; ASTM D790
Izod Impact, Unnotched 4.27 J/cm
8.00 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 43.0 J
31.7 ft-lb
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Specific Heat Capacity 1.17 J/g-°C
0.280 BTU/lb-°F
ASTM C351
Deflection Temperature at 0.46 MPa (66 psi) 143 °C

@Thickness 6.40 mm
 289 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 136 °C

@Thickness 6.40 mm
 277 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 V-0

@Thickness 5.99 mm
 V-0

@Thickness 0.236 in
 UL 94
5VA

@Thickness 5.99 mm
 5VA

@Thickness 0.236 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.50e+17 ohm-cm
2.50e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.10e+17 ohm
>= 1.10e+17 ohm
ASTM D257
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
 2.5

@Frequency 1.00e+6 Hz
 ASTM D150
2.52

@Frequency 100 Hz
 2.52

@Frequency 100 Hz
 ASTM D150
Dissipation Factor 0.00080

@Frequency 100 Hz
 0.00080

@Frequency 100 Hz
 ASTM D150
0.0052

@Frequency 1.00e+6 Hz
 0.0052

@Frequency 1.00e+6 Hz
 ASTM D150
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20%
FOAM - Flame Class Minimum Density 0.85g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction 10%
FOAM - MECHANICAL 6.4 mm Wt Reduction 10%
FOAM - PHYSICAL 6.4mm Wt Reduction 10%
FOAM - THERMAL 6.4mm Wt Reduction 10%