SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Opaque PC-Siloxane copolymer with excellent processability. UV stabilized. UL rated V-0/5VA/CTI-PLC-2. Available in limited colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | Type I, 50 mm/min; ASTM D638 |
| 100 % | 100 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.15 GPa | 312 ksi | 50 mm/min; ASTM D638 |
| 2.15 GPa | 312 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.15 GPa | 312 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D256 |
| 4.50 J/cm @Temperature -50.0 °C |
8.43 ft-lb/in @Temperature -58.0 °F |
ASTM D256 | |
| 5.50 J/cm @Temperature -30.0 °C |
10.3 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*3; ISO 180/1A |
| 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 7.00 J/cm² | 33.3 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 145 °C | 293 °F | Rate B/50; ISO 306 |
| 147 °C | 297 °F | Rate B/120; ISO 306 | |
| 147 °C | 297 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 | |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 | |
| Glow Wire Test | 900 °C | 1650 °F | IEC 60695-2-13 |
| 960 °C @Thickness 0.800 - 3.00 mm |
1760 °F @Thickness 0.0315 - 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A | |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Flint Hills P4C5B-075 Homopolymer Polypropylene
- LG Chemical LUCON CP510F PC/ABS+CNT
- LATI Kelon® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized
- Saint-Gobain CHR® 2254-2 High Modulus PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- DuPont Teijin Films Mylar® 854 Polyester Packaging Film, 60 Gauge
- 3D Systems Accura® 55 Plastic for SLA® Systems
- Arlon 30600R025 0.025" (0.635 mm) Uncured Unsupported Silicone Rubber on Release Carrier
- Beijing Evergrow Resources ER-W-85G Polypropylene Super-Fine Filter Material
- Addiplast Addilene H 462 M20 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved