Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 - 1.05 g/cc | 1.03 - 1.05 g/cc | |
| Density | 0.0297 g/cc | 0.00107 lb/in³ | Based on 35 times expansion |
| Bead Size | 0.350 - 0.500 mm | 0.0138 - 0.0197 in | JIS Z8801 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 2.50 MPa | 363 psi | @ 25 kg/m<sup>2</sup>; ASTM DC201 |
| Compressive Strength | >= 1.20 MPa | >= 174 psi | @ 25 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | 6.0 - 7.0 % | 6.0 - 7.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blocking | <2% | |
| Expandability | 35 Times | Expansion for 5 min Cheil Method |
| Fusion | >60% | Cheil Method |
| Polymer Content | 93-94% |
Users viewing this material also viewed the following:
- MV Labs AL900 AlPO4 Aluminum phosphate
- Polymax® Maxelast® C4903 TPE, Transparent
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled
- LG Chemical SG-950 Alphalac Polystyrene
- SABIC Innovative Plastics Valox® V3900WX PBT+PC (Asia Pacific)
- A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy
- 3M Dyneon™ FPO 3741 Fluoroelastomer
- Arlon R33468A030 0.0305" (0.775 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ TF 2029Z PTFE Fine Powder
Copyright © lookpolymers.com All Rights Reserved