- SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D 570 |
| Moisture Absorption at Equilibrium | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 |
| 0.13 % | 0.13 % | 50% RH; ASTM D 570 | |
| 0.28 % @Temperature 23.0 °C |
0.28 % @Temperature 73.4 °F |
ASTM D 570 | |
| 0.040 % @Time 86400 sec |
0.040 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Water Absorption at Saturation | 0.27 % @Temperature 23.0 °C |
0.27 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 1.20 kg, Temperature 300 °C |
13 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 14.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
14.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D 785 |
| Hardness, Rockwell M | 93 | 93 | ASTM D 785 |
| Hardness, H358/30 | 128 MPa | 18600 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
| 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.300 J/cm @Temperature 23.0 °C |
0.562 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.300 J/cm @Temperature -30.0 °C |
0.562 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 4.70 J/cm² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 30.0 J @Temperature 23.0 °C |
22.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; ASTM D 1044 |
| 10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | ASTM C 351 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C 177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | |
| Hot Ball Pressure Test | <= 140 °C | <= 284 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ISO 306 |
| 139 °C | 282 °F | Rate B/50; ASTM D 1525 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.584 | 1.584 | ASTM D 542 |
| 1.584 | 1.584 | ISO 489 | |
| Haze | <= 0.80 % @Thickness 2.54 mm |
<= 0.80 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | H | ASTM D 3363 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1281-47 VE SMC
- Gouda Vuurvast AK 70 K Dense Refractory Brick
- Mearthane Durethaneâ„¢ S DS-550D Solid Polyurethane Elastomer
- Lanxess Durethan® B 35 F 000000 Nylon 6, Extrusion, Low Viscosity
- Solvay Specialty Polymers Veradel® 3200P Polyethersulfone (PESU)
- Styron EMERGEâ„¢ 4600-10 Polycarbonate
- A. Schulman POLYBATCH™ Lattice Green 30155U Concentrate Based In LLDPE
- Chosun Refractories A40 Special High-Density Gunning Castable
- BCC Products MB 4000 RED Urethane Foundry Plank
Copyright © lookpolymers.com All Rights Reserved