SABIC Innovative Plastics Lexan® 123HSR PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® 123HSR PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, UV stabilised, super release grade polycarbonate.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 143 % | 143 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 126 µm/m-°C @Temperature -40.0 - 60.0 °C |
70.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 133 °C @Thickness 6.40 mm |
271 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 645 Reactive Alumina
- Osprey Metals 304L Stainless Steel Powder (Grade 90% - 22)
- NOVA Chemicals Novapol® TR-0735-U Hexene MDPE Rotational Molding Resin
- Johnson Matthey F Bronze High Temperature Alloy for Tungsten Carbide Brazing
- Huntsman MY 9612 Multifunctional Resin
- Styron INSPIREâ„¢ TF0808S(U) Polypropylene
- Techmer ES HiFill FR® PP CO FR HS
- BASF Paliotol™ Yellow K 1841 Color Additive
Copyright © lookpolymers.com All Rights Reserved