SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port, China |
| Download PDF |
SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Europe-Africa-Middle East).pdf
|
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical burn and OEM toxicity requirements. LEXAN CFR5630D resin is available in 5 prematched diffusion colors.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.110 % | 0.110 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.14 % | 0.14 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0055
- 0.0075
cm/cm <br>@Thickness 3.20 mm
|
0.0055
in/in <br>@Thickness 0.126 in
|
SABIC Method |
| Linear Mold Shrinkage, Transverse |
0.0060
- 0.0080
cm/cm <br>@Thickness 3.20 mm
|
0.0060
in/in <br>@Thickness 0.126 in
|
SABIC Method |
| Melt Flow |
5.0
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
5.0
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
| Melt Index of Compound |
5.0
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
5.0
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 |
| 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 23 % | 23 % | 50 mm/min; ISO 527 |
| 51 % | 51 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| 2.50 GPa | 363 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 103 MPa | 14900 psi | 2 mm/min; ISO 178 |
| 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
|
0.850
J/cm <br>@Temperature -30.0 °C
|
1.59
ft-lb/in <br>@Temperature -22.0 °F
|
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
|
NB
<br>@Temperature -30.0 °C
|
NB <br>@Temperature -22.0 °F
|
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*3; ISO 180/1A |
|
9.00
kJ/m² <br>@Temperature -30.0 °C
|
4.28
ft-lb/in² <br>@Temperature -22.0 °F
|
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
|
NB
<br>@Temperature -30.0 °C
|
NB <br>@Temperature -22.0 °F
|
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 13.2 J/cm² | 62.8 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
|
12.9
J/cm² <br>@Temperature -30.0 °C
|
61.4
ft-lb/in² <br>@Temperature -22.0 °F
|
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
|
0.900
J/cm² <br>@Temperature -30.0 °C
|
4.28
ft-lb/in² <br>@Temperature -22.0 °F
|
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy |
66.0
J <br>@Temperature 23.0 °C
|
48.7
ft-lb <br>@Temperature 73.4 °F
|
ASTM D3763 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow |
66.0
µm/m-°C <br>@Temperature -40.0 - 40.0 °C
|
36.7
µin/in-°F <br>@Temperature -40.0 - 104 °F
|
ASTM E 831 |
|
72.0
µm/m-°C <br>@Temperature 23.0 - 80.0 °C
|
40.0
µin/in-°F <br>@Temperature 73.4 - 176 °F
|
ISO 11359-2 | |
| CTE, linear, Transverse to Flow |
70.0
µm/m-°C <br>@Temperature -40.0 - 40.0 °C
|
38.9
µin/in-°F <br>@Temperature -40.0 - 104 °F
|
ASTM E 831 |
|
76.0
µm/m-°C <br>@Temperature 23.0 - 80.0 °C
|
42.2
µin/in-°F <br>@Temperature 73.4 - 176 °F
|
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
131
°C <br>@Thickness 3.20 mm
|
268
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
120
°C <br>@Thickness 3.20 mm
|
248
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| Vicat Softening Point | 136 °C | 277 °F | Rate B/50; ASTM D1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Oxygen Index | 45 % | 45 % | ISO 4589 |
| Glow Wire Test | 875 °C | 1610 °F | IEC 60695-2-13 |
|
960
°C <br>@Thickness 1.00 mm
|
1760
°F <br>@Thickness 0.0394 in
|
IEC 60695-2-12 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Pass | IEC 60695-10-2 | |
| FAA Flammability, FAR 25.853 A/B | PASSES | FAR 25.853 | |
| NBS Smoke Density, Flaming, Dmax | 70 | ASTM E 662 | |
| UV-light, water exposure/immersion | F1 | UL 746C | |
| Vertical Burn a (60s) passes at | 5sec | FAR 25.853 | |
| Vertical Burn b (12s) passes at | 5sec | FAR 25.853 |
| Chemical Resistance Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant |
2.79
<br>@Frequency 1.00e+9 Hz
|
2.79 <br>@Frequency 1.00e+9 Hz
|
ASTM ES 7-83 |
| Dissipation Factor |
0.0058
<br>@Frequency 1.10e+9 Hz
|
0.0058 <br>@Frequency 1.10e+9 Hz
|
ASTM ES 7-83 |
Users viewing this material also viewed:
- Lubriplate 930-AAA Bentone Type Multi-Purpose Grease
- Kraton® FG1901 G (SEBS) Linear Block Copolymer
- Hexcel® HexPly® M18/1 180°C Curing Epoxy Matrix
- ChevronTexaco ParaMount™ 1005 Paraffinic Process Oil
- CTC X-PRO CTC PP1020 Polypropylene Homopolymer
- Braskem GM5240PR HDPE High Density Extrusion Polyethylene
- BASF Ultramid® A3WG3 15% Glass Filled PA66 (Conditioned)
- Bhansali Engineering Abstron AN450M Flame Retardant ABS
- SABIC Innovative Plastics LNP Verton PV00A PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved