SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | |
| Moisture Absorption | 3.06 % | 3.06 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0188 cm/cm @Time 86400 sec |
0.0188 in/in @Time 24.0 hour |
ISO 294 |
| 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm @Time 86400 sec |
0.018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0182 cm/cm @Time 86400 sec |
0.0182 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
| 39.0 MPa | 5660 psi | ISO 527 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ISO 527 |
| 44.0 MPa | 6380 psi | ASTM D638 | |
| Elongation at Break | 32.3 % | 32.3 % | ISO 527 |
| 54.4 % | 54.4 % | ASTM D638 | |
| Elongation at Yield | 11.9 % | 11.9 % | ISO 527 |
| 14.8 % | 14.8 % | ASTM D638 | |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| 1.85 GPa | 268 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| 54.0 MPa | 7830 psi | ASTM D790 | |
| Flexural Modulus | 1.54 GPa | 223 ksi | ISO 178 |
| 1.60 GPa | 232 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 32.0 J | 23.6 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 18.0 J | 13.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature -40.0 - 40.0 °C |
75.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 135 µm/m-°C @Temperature -40.0 - 40.0 °C |
75.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 149 µm/m-°C @Temperature -40.0 - 40.0 °C |
82.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 149 µm/m-°C @Temperature -40.0 - 40.0 °C |
82.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-MUTE 9000 Microwave Absorber
- Mar-Bal MB1000-25 Thermoset Polyester Composite Molding Compound
- Materion Beryllium Copper Alloy 25 Wire; HT (TH04) Temper; 1.3-2.0 mm Diameter (UNS C17200)
- Solvay Specialty Polymers KetaSpire® KT-820FP Polyetheretherketone (PEEK)
- SCG Chemicals EL-Leneâ„¢ H511W High Density Polyethylene Wire & Cable Grade
- UBE UBEPOL VCR406 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Elastomer Engineering Elastamide 100 Elastomer Modified RIM Nylon 6
- 3M Scotchcal™ ElectroCut™ 7725-15 Graphic Film
- A. Schulman PP 1930L-01 Polypropylene Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved