Arlon T4020-R002 0.020" Cured, Fusible Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon T4020-R002 0.020" Cured, Fusible Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

0.5 inch wide, 20 mil thick, red, rectangular cross-section, fusible silicone tape.Design/Construction:Side 1: Cured Fusible Silicone RubberSubstrate: 15% Sinusoidal FiberglassSide 2: Cured Fusible Silicone RubberInterleave: 1 mil Polyester FilmThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	203 microns	8.00 mil	Substrate; Arlon SQA-TMS-012
	508 microns	20.0 mil	Overall thickness; Arlon SQA-TMS-012

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	50	50	Silicone Property; ASTM D2240
Tensile Strength	9.65 MPa	1400 psi	Silicone Property; ASTM D412
Elongation at Break	20 %	20 %	Tape Property; Arlon SQA-TMS-048
	702 %	702 %	Silicone Property; ASTM D412
Tear Strength	23.0 kN/m	131 pli	Die B; Silicone Property; ASTM D624
Peel Strength	0.929 kN/m	5.30 pli	Adhesion Strength; Arlon SQA-TMS-047

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	22.4 kV/mm	570 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Shelf Life	12.0 Month @Temperature 21.1 °C	12.0 Month @Temperature 70.0 °F

Descriptive Properties	Value	Comments
Color	Naturally White	Substrate
	Red	Product
Tensile Strength (Lb/in)	79	Tape Property; Arlon SQA-TMS-048