Diamond Polymers DIAMALOY GLY 7510 High Heat ASA Weatherable Polymer

Category	Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer	Diamond and Network Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Diamond Polymers DIAMALOY GLY 7510 High Heat ASA Weatherable Polymer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Diamaloy GLY 7510 resin is a high gloss, high heat and high impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. This product is rated f1 by UL and be customed colored.Applications:Typical applications include those requiring weatherability and toughness for automotive exterior applications and lawn and garden applications. As with any product, use of Diamaloy GLY 7510 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D955
Melt Flow	4.0 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C	4.0 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F	ASTM D1238
	8.3 g/10 min <br>@Load 5.00 kg,<br> Temperature 260 °C	8.3 g/10 min <br>@Load 11.0 lb,<br> Temperature 500 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	101	101	ASTM D785
Tensile Strength at Break	38.0 MPa	5510 psi	chs 2.0 in/min; ASTM D638
Tensile Strength, Yield	52.0 MPa	7540 psi	chs 2.0 in/min; ASTM D638
Elongation at Break	22 %	22 %	chs 2.0 in/min; ASTM D638
Elongation at Yield	3.0 %	3.0 %	chs 2.0 in/min; ASTM D638
Tensile Modulus	2.784 GPa	403.8 ksi	chs 2.0 in/min; ASTM D638
Flexural Strength	79.0 MPa <br>@Thickness 3.17 mm	11500 psi <br>@Thickness 0.125 in	chs 0.05 in/min; 2 in span; ASTM D790
Flexural Modulus	2.432 GPa <br>@Thickness 3.17 mm	352.7 ksi <br>@Thickness 0.125 in	chs 0.05 in/min; ASTM D790
Izod Impact, Notched	0.427 J/cm <br>@Thickness 3.17 mm,<br> Temperature -30.0 °C	0.800 ft-lb/in <br>@Thickness 0.125 in,<br> Temperature -22.0 °F	ASTM D256
	2.46 J/cm <br>@Thickness 3.17 mm,<br> Temperature 23.0 °C	4.61 ft-lb/in <br>@Thickness 0.125 in,<br> Temperature 73.4 °F	ASTM D256
Impact Test	20.8 J <br>@Temperature -30.0 °C	15.3 ft-lb <br>@Temperature -22.0 °F	Total Energy; ASTM D3763
	27.0 J <br>@Temperature 23.0 °C	19.9 ft-lb <br>@Temperature 73.4 °F	Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear	75.6 µm/m-°C <br>@Temperature -40.0 - 37.8 °C	42.0 µin/in-°F <br>@Temperature -40.0 - 100 °F	ASTM E831
CTE, linear, Transverse to Flow	86.4 µm/m-°C <br>@Temperature -40.0 - 37.8 °C	48.0 µin/in-°F <br>@Temperature -40.0 - 100 °F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	102 °C	216 °F	0.125";; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	88.0 °C	190 °F	0.125";; ASTM D648
Vicat Softening Point	104 °C	219 °F	ASTM D1525
Flammability, UL94	HB <br>@Thickness 1.52 mm	HB <br>@Thickness 0.0600 in

Optical Properties	Metric	English	Comments
Gloss	94 %	94 %	Untextured; 60°; ASTM D523

Electrical Properties	Metric	English	Comments
Hot Wire Ignition, HWI	3.0 sec	3.0 sec	PLC Code; ASTM 746A
High Amp Arc Ignition, HAI	0.00 arcs	0.00 arcs	PLC Code; ASTM 746A