SABIC Innovative Plastics Lexan® 135 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® 135 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose low flow polycarbonate powder gradeThis data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ASTM D 570 |
| 0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | >= 70 % | >= 70 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 9.07 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 64.0 J @Temperature 23.0 °C |
47.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C 351 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 154 °C | 309 °F | Rate B/50; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- GEHR Plastics ABS Acrylonitrile Butadiene Styrene
- Isoflon PTFE + 15% Graphite Polytetrafluoroethylene with 15% Graphite
- LG Chemical LUTENE CCO550BK PE Compound
- SABIC Innovative Plastics LNP THERMOCOMP MF006A PP (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® TF-0956 HI-PMMA
- ExxonMobil Mobilgrease 28
- Ashley Polymers Ashlene® 980LS-33G Nylon 612, 33% Glass Reinforced
- ATI Allvac® VascoMax® T-250 Specialty Steel, Heat Treatment: 816°C (1500°F) + Age
- A.D. Compound Adene NCZA Homopolymer 70% CaCO3 Filled Polypropylene
Copyright © lookpolymers.com All Rights Reserved