Shuman 791 Black and Custom Colors ABS-Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Shuman |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shuman 791 Black and Custom Colors ABS-Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Long term thermal aging rated. Excellent flame retardancy, good impact strength, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Izod Impact, Notched | 2.14 J/cm | 4.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 93.0 µm/m-°C @Temperature 20.0 °C |
51.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL746-B |
| UL RTI, Mechanical with Impact | 70.0 °C | 158 °F | UL746-B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL746-B |
| Flammability, UL94 | V-1 @Thickness 2.54 mm |
V-1 @Thickness 0.100 in |
UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V | 250 V | UL 746A |
| Hot Wire Ignition, HWI | 33.4 sec | 33.4 sec | UL746A |
| High Amp Arc Ignition, HAI | 199.4 arcs | 199.4 arcs | UL746A |
| High Voltage Arc-Tracking Rate, HVTR | 149.0 mm/min | 5.866 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 177 - 216 °C | 351 - 421 °F | Extrusion |
| 204 - 227 °C | 399 - 441 °F | Injection |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DL002F PC
- DuPont Nucrel® 30707SR Ethylene-Acrylic Acid Copolymer Resin for Film and Extrusion Coating (discontinued **)
- PolyOne Dynaflex™ G7690-1 (Natural) Thermoplastic Elastomer (TPE)
- Momentive Performance Materials HV 3/506 Heat Cured Rubber - High Temperature
- Solvay MACKINE® 401 Surfactant
- DuPont Bynel® 50E571 Anhydride-Modified Polypropylene Adhesive Resin
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- Arlon 55191R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Ashley Polymers Ashlene® N541L Nylon 66
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Translink 555
Copyright © lookpolymers.com All Rights Reserved