SABIC Innovative Plastics LNP STAT-KON DX06500 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX06500 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX06500 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Glass Fiber. Added features of this material include: Electrically Conductive, Wear Resistant, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm @Time 86400 sec |
0.0028 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0047 cm/cm @Time 86400 sec |
0.0047 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527 |
| 119 MPa | 17300 psi | ASTM D638 | |
| Tensile Strength, Yield | 117 MPa | 17000 psi | ISO 527 |
| 119 MPa | 17300 psi | ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| 1.7 % | 1.7 % | ISO 527 | |
| Elongation at Yield | 1.7 % | 1.7 % | ASTM D638 |
| 1.7 % | 1.7 % | ISO 527 | |
| Tensile Modulus | 12.33 GPa | 1788 ksi | 1 mm/min; ISO 527 |
| 13.78 GPa | 1999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 177 MPa | 25700 psi | ISO 178 |
| 186 MPa | 27000 psi | ASTM D790 | |
| Flexural Modulus | 10.6 GPa | 1540 ksi | ISO 178 |
| 11.72 GPa | 1700 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.19 J/cm | 11.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SF82TF20 Silver-coated Glass Fibers
- Ravago Manufacturing Americas Hylon® N2233HL BK Nylon 6
- SGL Carbon Group PANOX® FA C063 SSC High performance Crimped staple oxidized textile fiber, For felts and non-wovens
- ExxonMobil Escorene® LD 755.12 Molding, extrusion and compounding resin
- Fainplast Compounds GA 80 Flexible PVC, Flame Retardant Sheathing
- Clariant Renol ABS3460 ABS, General Purpose, Low Gloss
- DuPont Performance Polymers Hytrel® SC956 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
- Arlon 30400R060 0.06" Uncured, Unsupported Silicone Rubber on Release Carrier
- Aptek 2205 A/B Low modulus urethane stacking compound
Copyright © lookpolymers.com All Rights Reserved