SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | <= 240 °C | <= 464 °F | IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
UL 94 |
| 5VA @Thickness 1.60 mm |
5VA @Thickness 0.0630 in |
UL 94 | |
| Glow Wire Test | 775 °C @Thickness 0.400 mm |
1430 °F @Thickness 0.0157 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 775 °C @Thickness 1.00 mm |
1430 °F @Thickness 0.0394 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 775 °C @Thickness 1.50 mm |
1430 °F @Thickness 0.0591 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 825 °C @Thickness 3.00 mm |
1520 °F @Thickness 0.118 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 0.400 mm |
1760 °F @Thickness 0.0157 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D 257 |
| Dielectric Strength | 16.0 kV/mm @Thickness 1.60 mm |
406 kV/in @Thickness 0.0630 in |
in air; ASTM D 149 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
Users viewing this material also viewed the following:
- NeXolve White Optionox® Polyimide Film
- SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer (Asia Pacific)
- DuPont Performance Polymers Hytrel® 7246HS BK320 TPC-ET (Unverified Data**)
- ICO Polymers ICORENEâ„¢ 110-1016 LMDPE Rotational Molding Resin
- SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific)
- Zhejiang Juner PA-A6-4 Non-Reinforced
- DuPont Vamac® GXF Sample Compound
- A. Schulman POLYBATCH™ White B8750A Concentrate Based In HDPE
Copyright © lookpolymers.com All Rights Reserved