Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 9.41 GPa | 1360 ksi | same value from ASTM and ISO test. |
|
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **)
Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527-2 |
|
Pasargad Polymer Peyvand Pasamid 3P-H1150B Nylon 6, 50% Glass Fiber Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
|
Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled
Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527 |
|
Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527-1/-2 |
|
Lanxess Durethan® BKV 130 GIT 900116 Copolyamide, 30% Glass Fiber
CoPA, injection molding grade, 30% glass fibers, elastomer-modified, suitable for GIT (gas assisted technology), good surface finishApplication Examples: Chain-saw handles, office chair armrests, of..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
|
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
|
LATI Latilub 66-01M G/30 PA66, 30% Glass Fiber Reinforced, Molybdenum disulphide Filled
Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
|
LATI Latishield 66-13A G/30 PA66, Steel/Glass Fiber Reinforced
EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527 Type 1A |
|
Solvay TECHNYL® A 218 V43 Black 21 N PA66, 43% glass fiber, Conditioned
Description: Polyamide PA66, reinforced with 43% of glass fiber, heat stabilized, for injection molding.Available in: North AmericaProduct Applications: TECHNYL® A 218 V43 is used in all sectors ..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12
LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
|
|||
| Tensile Modulus | 9.36 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON DE0021E PC
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive.
|
|||
| Tensile Modulus | 9.36 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON DE0021E PC (Asia Pacific)
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific)
High flow Ultem for thin wall application
|
|||
| Tensile Modulus | 9.38 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON DX01303C PC
LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON ZX97172 PPE+PS (Europe-Africa-Middle East)
Electrically Conductive PPE+PS Blend Compound, containing a proprietary filler system.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS
LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead.
|
|||
| Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12
LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66
LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
|
Plenco 2311 Phenolic, Granular, Compression Molded
PLENCO 02311 is a versatile general purpose organic filled phenolic molding compound offering excellent mold processability and optimized cure cycles. PLENCO 02311 is also granulated to provide impr..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
|
Plenco 4349 Phenolic, Granular, Injection Molded
PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer ..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
|
Plenco 7507 Phenolic, Granular, Compression Molded
PLENCO 07507 is an organic reinforced phenolic molding compound offering improved dimensional stability under humid conditions. 07507 offers excellent resistance to degradation from detergent solut..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | dry; ISO 527-1/-2 |
|
EMS-Grivory Grivory® BG-30 EC PA6-GF30
Information provided by EMS Grivory
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Staramide A24G6K PA66, 30% Glass Fiber Reinforced, Heat stabilized, Injection Molding
Staramide A24G6K is an Easy Flow, Heat and Hydrolytically Stabilized, 30% Glass Fiber Reinforced, Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Staramide AG6H PA66, 30% Glass Filled, Injection Molded
AG6 is a Heat Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Staramide AG6K PA66, 30% Glass Filled, Injection Molded
AG6 is a Heat and Hydrolytically Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Staramide RF006SXP PA66, 30% Glass Fiber Filled, Injection Molded
Staramide RF006SXP is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Staramide RF006SXS PA66, 30% Glass Fiber Filled, Injection Molded
Staramide RF006SXS is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar.
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
|
Eurostar Starflam RF0057E PA66, 25% Glass Filled, Injection Molded
Starflam PF0057E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z270EM)Information provided by Polym..
|
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
|
LATI Latilub 66-15ST G/30 PA66, 30% Glass Fiber Reinforced, Silicone/PTFE Filled
Self-lubricating product based on Polyamide 66 (PA66). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La..
|
|||
| Tensile Modulus |
9.40
GPa <br>@Temperature 23.0 °C
|
1360
ksi <br>@Temperature 73.4 °F
|
DAM; ISO 527 |
|
DuPont Performance Polymers Zytel® 73G30TGI BK267 Nylon 6
(Unverified Data**)
Zytel® 73G30TGI BK267 is a 30% glass fiber reinforced, toughened, black polyamide 6 optimized for gas injection molding process.Information provided by DuPont Performance Polymers
|
|||