SABIC Innovative Plastics LNP THERMOCOMP MF006AS PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF006AS PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MF006AS is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| 1.6 % | 1.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.92 GPa | 1000 ksi | 1 mm/min; ISO 527 |
| 7.77 GPa | 1130 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Yield Strength | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.01 GPa | 872 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.64 J/cm | 4.95 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 26.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP640S Injection Molding Grade Polypropylene
- Ferro EG 4020 Display Device
- Kraton® Cariflex™ IR0310 K Polyisoprene
- Shandong Rike Chemical RIKEâ„¢ RK-521 MBS Impact Modifier for PVC Transparent Product
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- A. Schulman POLYBATCH™ Ivory 90033/4 Concentrate Based In LDPE
- Tisan TISESTER® 15% Glass Fiber Reinforced and Heat Stabilized Polybutylene Terephthalate
- A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
- 3M Bumpon™ SJ6232 Resilient Rollstock
Copyright © lookpolymers.com All Rights Reserved