- Lucent Polymers PC/ABS-1208 Polycarbonate+ABS, General Purpose, Injection Grade
Lucent Polymers PC/ABS-1208 Polycarbonate+ABS, General Purpose, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PC/ABS-1208 Polycarbonate+ABS, General Purpose, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.17 MPa | 8002 psi | ASTM D638 |
| Elongation at Break | >= 140 % | >= 140 % | ASTM D638 |
| Flexural Strength | 84.14 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 2.310 GPa | 335.1 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107.22 °C | 225.00 °F | ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products FT7013-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Premix Thermoplastics PRE-ELEC® PE 1308 (discontinued **)
- Huntsman IROGRAN® A 85 D 4968 Polyester-Based TPU-Injection Extrusion Grade
- Fiberfil® J-60/30/E Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- SABIC Innovative Plastics Noryl RF1132 PPE+PP
- UBE UBESTA® 3030U Nylon 12 (After Ethanol for 1000 hours)
- ExxonMobil LDPE LD 104BR Low Density Polyethylene Resin
- Adamas Rixon U PEEK, Unreinforced
Copyright © lookpolymers.com All Rights Reserved