- Acetal Copolymer, 10% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer
SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced , Acetal Copolymer, PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KFL32R is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Easy Release, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.330 % | 0.330 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0108 cm/cm @Time 86400 sec |
0.0108 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0134 cm/cm @Time 86400 sec |
0.0134 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ASTM D638 |
| 79.0 MPa | 11500 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Tensile Modulus | 5.10 GPa | 740 ksi | 50 mm/min; ASTM D638 |
| 5.40 GPa | 783 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| 122 MPa | 17700 psi | ISO 178 | |
| Flexural Modulus | 4.82 GPa | 699 ksi | ASTM D790 |
| 5.80 GPa | 841 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREADD PA 143 (discontinued **)
- KB Alloys Tibor® 3% Ti - 0.2% B Titanium Boron Aluminum Alloy
- Fujipoly Industries FLAT-5TV-12-.75 silicone rubber fusible tape
- LTL Color Compounds ColorRxâ„¢ ABS-0500RX Biocompatible ABS
- LyondellBasell Adsylâ„¢ 3 C 30 F HP Polypropylene Copolymer
- Lehmann & Voss LUVOCOM® 100-7846 Thermoplastic polyurethane, with aramid reinforcement
- SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+HIPS (Europe-Africa-Middle East)
- Hexcel® HexForce™ 7627 Fiber Glass Fabric
- Chevron Phillips K-Resin® KR01 Styrene-Butadiene Copolymer, Injection Molding Grade
- ExxonMobil Exterex™ TM111 Synthetic Fluid
Copyright © lookpolymers.com All Rights Reserved