Polymer Property : Tensile Modulus = 1000 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	6.90 GPa	1000 ksi
Plastcom SLOVAMID 6 GF 25 FRC 3 PA6, 25% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically strengthened with 25 % glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering an..
Tensile Modulus	6.90 GPa	1000 ksi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP6GF33 Nylon 6, 33% Glass Reinforced, Conditioned Nylon 6 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Tensile Modulus	6.89 GPa	1000 ksi	ASTM D638
Quadrant EPP Ketron® GF30 PEEK, Extruded 30% Glass-Reinforced Polyetherether Ketone (ASTM Product Data Sheet)
Tensile Modulus	6.90 GPa	1000 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP CX05031 PS (Europe-Africa-Middle East) LNP* Lubricomp* CX05031 is a compound based on Polystyrene resin containing Graphite, Silicone. Added features include; Internally Lubricated.
Tensile Modulus	6.90 GPa	1000 ksi	ASTM D638
PolyOne Edgetek® ES-20GF-15GM/000 Polyethersulfone - 20% Glass Fiber - 15% Milled Glass (discontinued **) Data provided by PolyOne.
Tensile Modulus	6.89 GPa	1000 ksi	ASTM D638
Quadrant EPP Ketron® GF30 LSG PEEK, Extruded 30% Glass-Reinforced Polyetherether Ketone (ASTM Product Data Sheet)
Tensile Modulus	6.92 GPa @Thickness 6.40 mm	1000 ksi @Thickness 0.252 in	ASTM D638
SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm).
Tensile Modulus	6.92 GPa	1000 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features include: Exceptional Processing, Non-Brominated & Non-Chlorinated Flame Retardant.
Tensile Modulus	6.90 GPa	1000 ksi	ASTM D638
Sumitomo Bakelite DurezÂ® 31735 Phenolic, Compression Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension..
Tensile Modulus	6.90 GPa	1000 ksi	ASTM D638
Sumitomo Bakelite DurezÂ® 31735 Phenolic, Injection Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension..
Tensile Modulus	6.90 GPa	1000 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-25 HM PA6-GF25 Product description: Grilon BG-25 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 25% glass fibers. Grilon BG-25 HM has the following important prop..
Tensile Modulus	6.90 GPa @Temperature 120 °C	1000 ksi @Temperature 248 °F	ISO 527-1/-2
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized
Tensile Modulus	6.89 GPa	1000 ksi	ASTM D638
Ensinger Tecatron® XP-61 Compression Molded PPS Compound, 25% Fiberglass and Mineral Filled Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p..
Tensile Modulus	6.90 GPa @Temperature -40.0 °C	1000 ksi @Temperature -40.0 °F	ISO Data
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Modulus	6.89 GPa	1000 ksi	Crosswise; ASTM D638
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Tensile Modulus	6.89 GPa	1000 ksi	Crosswise; ASTM D638
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Tensile Modulus	6.91 GPa	1000 ksi	same value from ASTM and ISO test.
BASF Capron® GR40 40% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR40 is a 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is also ava..
Tensile Modulus	6.92 GPa	1000 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66 Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	6.89 GPa	1000 ksi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® ATH-30GF/000 Acetal-Homopolymer, Glass Filled (discontinued **) Description/Features:Glass Fiber ReinforcedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.