SABIC Innovative Plastics LNP THERMOCOMP 67002XXH PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 67002XXH PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 67002XXH is a compound based on PBT+PC containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added features include: Low antimicrobial performance, high impact, heat and chemical resistance. Improved retention of mechanical properties under UV exposure.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| 105 % | 105 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 5 mm/min; ASTM D638 |
| 4.6 % | 4.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| 2.12 GPa | 307 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.95 GPa | 283 ksi | 2 mm/min; ISO 178 |
| 2.11 GPa | 306 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Impact Test | 66.0 J | 48.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nylene® 453 Nylon 6
- 3M Dyneon™ Fluorel™ FE-5622Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Shandong Dongyue Shenzhou New Material Co CHFM 200 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- Hexcel® HexPly® F515 Epoxy Resin
- Chevron Phillips Marlex® 9512H - 9513H High Performance Series HDPE Blow Molding Resin
- ExxonMobil Mobil Rarus 824
- CIMBAR FlexTalc® 1222D Ultrafine Talc for TPO Applications, Densified
- ExxonMobil Label-Lyte™ 150LL-302 OPP Film
- Nye Lubricants 2001A (SO) Synthetic Oil
- China-Yixing Longly Refractories 95 Alumina Ceramic
Copyright © lookpolymers.com All Rights Reserved