Techmer ES LuriblendÂ® PC CF15 TL6 BK 15% Carbon Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Carbon Fiber Filler , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer	Techmer ES
Trade Name	Luriblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES LuriblendÂ® PC CF15 TL6 BK 15% Carbon Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.31 g/cc	0.0473 lb/inÂ³	ASTM D792
Water Absorption	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Thickness 3.17 mm	0.0030 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Yield	112 MPa	16200 psi	ASTM D638
Elongation at Break	5.0 %	5.0 %	ASTM D638
Flexural Yield Strength	159 MPa	23000 psi	ASTM D790
Flexural Modulus	8.62 GPa	1250 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Thickness 3.17 mm	1.00 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	3.20 J/cm @Thickness 3.17 mm	6.00 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	19.8 Âµm/m-Â°C	11.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	144 Â°C	292 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	139 Â°C	283 Â°F	Unannealed; ASTM D648
Flammability, UL94	V-2	V-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	10000 ohm-cm	10000 ohm-cm	ASTM D257
Surface Resistance	1e+05	1e+05	ASTM D257