NYCOA 446 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 446 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UL-94 V-2 rated for flammability extrusion grade for rod, sheet and filmInformation provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM D638 |
| Elongation at Break | >= 25 % | >= 25 % | ASTM D638 |
| Flexural Yield Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.700 mm |
V-2 @Thickness 0.0276 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 225 °C | 437 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- Kazanorgsintez 102-274 Thermostabilized Low Density Polyethylene Composition for Radiation Modification
- Indium Corp. #1010 Wave Solder Flux, Water-Soluble
- KKPC KOSYN 1712C Styrene Butadiene Rubber
- Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6
- A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT
- Dow Corning SYLGARD® PMCP309 Silicone Surfactant
- 3M SJ5500 Protective Product, Molded Shapes
- Bulk Molding Compounds BMC 901 Encapsulating Grade Molding Compound
- ATI Allvac® 3-2.5 Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
- Orion Engineered Carbons CORAX® HP 160 HP Carbon Black
Copyright © lookpolymers.com All Rights Reserved