Supreme Petrochem SP 6530 Antistatic Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 6530 Antistatic Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Prevents dust patterns due to static charges Eliminates need of coatings Fully colorable Processing Injection molding Extrusion & Forming Applications Meter housings Foodservice ware Office accessories Electrical Enclosures Material Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 200 °C |
18 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.1 MPa | 3060 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 39.2 MPa @Thickness 3.20 mm |
5690 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.91 GPa @Thickness 3.20 mm |
277 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.20 mm |
1.69 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Vicat Softening Point | 89.0 °C | 192 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 - 1.00e+15 ohm-cm | 1.00e+14 - 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 - 1.00e+16 ohm | 1.00e+13 - 1.00e+16 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 230 °C | <= 446 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | ( 2 hrs) Pre drying temp. |
Users viewing this material also viewed the following:
- M Chemical GUARD DOGâ„¢ UV770 HALS Light Stabilizer
- Materion Beryllium Copper Alloy 10 Rod and Bar; A (TB00) Temper; All Sizes (UNS C17500)
- SABIC Innovative Plastics LNP STAT-KON DE0026 PC (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- ExxonMobil Enable™ 20-10CB Metallocene Polyethylene Resin (European Grade)
- Barlog Plastics KEBAFORM C 901 LF POM Copolymer unreinforced, improved wear and friction
- Asahi Kasei Tenac® SH210 Homopolymer Acetal Resin
- Polyplastics Duracon® EB-08 Acetal Co-polymer (POM), Conductive, Antistatic
Copyright © lookpolymers.com All Rights Reserved