SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Carbon Fiber Filled , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* Cycoloy_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0020 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 17 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 95.0 MPa
13800 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.9 %
1.9 %
Type I, 5 mm/min; ASTM D638
1.9 %
1.9 %
5 mm/min; ISO 527
Elongation at Yield 1.9 %
1.9 %
Type I, 5 mm/min; ASTM D638
1.9 %
1.9 %
5 mm/min; ISO 527
Tensile Modulus 7.50 GPa
1090 ksi
1 mm/min; ISO 527
7.58 GPa
1100 ksi
5 mm/min; ASTM D638
Flexural Strength 144 MPa
20900 psi
1.3 mm/min, 50 mm span; ASTM D790
145 MPa
21000 psi
2 mm/min; ISO 178
Flexural Yield Strength 145 MPa
21000 psi
2 mm/min; ISO 178
Flexural Modulus 6.20 GPa
899 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.38 GPa
925 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.47 J/cm
6.50 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 82.0 J

@Temperature 23.0 °C
 60.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 14.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
26.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 14.4 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
74.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 41.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C

@Thickness 3.20 mm
 207 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C

@Thickness 3.20 mm
 198 °F

@Thickness 0.126 in
 unannealed; ASTM D648
94.0 °C

@Thickness 6.40 mm
 201 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 101 °C
214 °F
Rate B/120; ISO 306
111 °C
232 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.990 mm
 V-0

@Thickness 0.0390 in
 UL 94
5VB

@Thickness 1.49 mm
 5VB

@Thickness 0.0587 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm
1000 ohm-cm
ASTM D257
Surface Resistance 1.00e+6 ohm
1.00e+6 ohm
ASTM D257
Static Decay 0.010 sec
0.010 sec
5000V to <50V; FTMS101B