SABIC Innovative Plastics LNP Lubricomp ML002S PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp ML002S PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 0.960 g/cc
0.960 g/cc
ASTM D 792
Density 0.950 g/cc
0.0343 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.030 %
0.030 %
23°C / 50% RH; ISO 62
0.020 %

@Time 86400 sec
 0.020 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.0 MPa
3190 psi
5 mm/min; ISO 527
27.0 MPa
3920 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 34.0 MPa
4930 psi
5 mm/min; ISO 527
35.0 MPa
5080 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 21.3 %
21.3 %
Type I, 5 mm/min; ASTM D 638
28.9 %
28.9 %
5 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
6.2 %
6.2 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 1.74 GPa
252 ksi
1 mm/min; ISO 527
2.14 GPa
310 ksi
50 mm/min; ASTM D 638
Flexural Strength 44.0 MPa
6380 psi
ISO 178
Flexural Modulus 1.67 GPa
242 ksi
2 mm/min; ISO 178
1.71 GPa
248 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.350 J/cm

@Temperature 23.0 °C
 0.656 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 6.96 J/cm

@Temperature 23.0 °C
 13.0 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 39.0 kJ/m²

@Temperature 23.0 °C
 18.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.66
0.66
ASTM D 3702 Modified
Coefficient of Friction, Static 0.60
0.60
ASTM D 3702 Modified
K (wear) Factor 32.2 x 10-8 mm³/N-M
16.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D 3702 Modified
469 x 10-8 mm³/N-M
233 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature -30.0 - 30.0 °C
 66.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 115 µm/m-°C

@Temperature -30.0 - 30.0 °C
 63.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C
201 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
119 °C

@Thickness 3.20 mm
 246 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
57.0 °C

@Thickness 3.20 mm
 135 °F

@Thickness 0.126 in
 unannealed; ASTM D 648