Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Saint-Gobain Perfomance Plastics |
| Trade Name | Meldin® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Meldin® 7001 CM unfilled polyimide base resin, compression moldedSpecification Qualifications:Satisfies Type I P for ASTM D 6456-99: Standard Specification for Finished Parts Made from Polyimide ResinSatisfies Class 1, Form P for SAE AMS 3644G: Polyimide, Molded Rod, Bar and Tube, Plaque, and Formed PartsSatisfies Type I P for MIL-R-46198: Resin, Polyimide, Hot Pressed or Pressed and SinteredInformation provided by Saint-Gobain Performance Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
ASTM D570 |
| 0.64 % @Time 173000 sec |
0.64 % @Time 48.0 hour |
ASTM D570 | |
| Deformation | 0.10 % | 0.10 % | 2000 psi load; ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 40 - 55 | 40 - 55 | ASTM D785 |
| Tensile Strength | 43.1 MPa @Temperature 260 °C |
6250 psi @Temperature 500 °F |
ASTM D638 |
| 58.6 MPa @Temperature 175 °C |
8500 psi @Temperature 347 °F |
ASTM D638 | |
| 68.9 MPa @Temperature 120 °C |
10000 psi @Temperature 248 °F |
ASTM D638 | |
| 86.2 MPa @Temperature 23.0 °C |
12500 psi @Temperature 73.4 °F |
ASTM D638 | |
| Elongation at Break | 5.0 % @Temperature 260 °C |
5.0 % @Temperature 500 °F |
ASTM D638 |
| 8.0 % @Temperature 23.9 °C |
8.0 % @Temperature 75.0 °F |
ASTM D638 | |
| Flexural Strength | 62.7 MPa @Temperature 260 °C |
9100 psi @Temperature 500 °F |
ASTM D790 |
| 109 MPa @Temperature 23.9 °C |
15800 psi @Temperature 75.0 °F |
ASTM D790 | |
| Flexural Modulus | 1.70 GPa @Temperature 260 °C |
247 ksi @Temperature 500 °F |
ASTM D790 |
| 3.10 GPa @Temperature 23.9 °C |
450 ksi @Temperature 75.0 °F |
ASTM D790 | |
| Compressive Yield Strength | 26.2 MPa @Strain 1.00 % |
3800 psi @Strain 1.00 % |
ASTM D695 |
| 128 MPa @Strain 10.0 % |
18500 psi @Strain 10.0 % |
ASTM D695 | |
| Compressive Modulus | 2.60 GPa | 377 ksi | ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.6 µm/m-°C @Temperature 23.9 - 260 °C |
27.0 µin/in-°F @Temperature 75.0 - 500 °F |
ASTM E831 |
| Thermal Conductivity | 0.346 W/m-K | 2.40 BTU-in/hr-ft²-°F | ASTM F433 |
| Oxygen Index | 100 % | 100 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 1.00e+15 - 1.00e+16 ohm | 1.00e+15 - 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.14 @Frequency 1.00e+6 Hz |
3.14 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.16 @Frequency 10000 Hz |
3.16 @Frequency 10000 Hz |
ASTM D150 | |
| 3.18 @Frequency 100 Hz |
3.18 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 22.8 kV/mm | 580 kV/in | short time 2 mm thick; ASTM D149 |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 6, Stainless Steel Filled
- Metabolix Mirelâ„¢ I6001 Biobased Polymeric Modifier
- Haysite 46000 Polyester SMC, 30% Glass Reinforced
- Schwartz Technical Plastics LAMIGAMID® 307 Cast Polyamide 6, Heat Stabilized, Conditioned
- Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, Conditioned
- A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy
- Dow AFFINITY™ SM 8250 Polyolefin Plastomer
- California Fine Wire Alloy 446 Precious Metal Alloy
- Aremco Pyro-Paint™ 634-ALP High Temperature Refractory Coating
- Kazanorgsintez PC-075D Polycarbonate
Copyright © lookpolymers.com All Rights Reserved