Polymer Property : Tensile Strength at Break = 3190 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D 638
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group.
Tensile Strength at Break	22.0 MPa	3190 psi	50 mm/min; ISO 527
Polimeri Europa Edistir RK 451G Polystyrene UL94 V-0, polybromobiphenylether (PBBE) free, flame retarded, high impact polystyrene. This grade combines medium flow, heat resistance and good light stability for injection moulding of technical p..
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Europe-Africa-Middle East) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Tensile Strength at Break	22.0 MPa	3190 psi
Plastcom SLOVALEN PC 93 T 20 PP, 20% mineral filling, UV stabilization FeaturesModified PP for injection moulding with the content of 20 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased..
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D638
Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer The Tritheva TN 2007 resin is an Ethylene-Vinyl Acetate copolymer (EVA), developed to meet the multi-layer packaging needs where are required high strength, with high toughness, and excellent optica..
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS LNP* LUBRICOMP* CBL36XXC is a compound based on Polystyrene resin containing 30% Glass Bead and 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527
FKuR Kunststoff Bio-FlexÂ® A 4100 CL Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Tensile Strength at Break	22.0 MPa	3190 psi
JPJ Technologies 6380M HDPE Extrusion Information provided by JPJ Technologies
Tensile Strength at Break	22.0 MPa	3190 psi
LATI Laticonther 52/11 CP1/600 F3 PP Homopolymer High thermal conductivity product based on Polypropylene homopolymer (PPh). Special filler. Potentially suitable for food/medical contact application.Availability: Africa & Middle East; Asia Pacific..
Tensile Strength at Break	22.0 MPa	3190 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the..
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant.
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific) LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications.
Tensile Strength at Break	22.0 MPa	3190 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp MB006SU PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MB006SU is a compound based on Polypropylene resin containing Glass Bead. Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Af..
Tensile Strength at Break	22.0 MPa	3190 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..
Tensile Strength at Break	22.0 MPa	3190 psi	25mm/min; ISO 527
Borealis LE0592 Polyethylene LE0592 is a crosslinkable black polyethylene compound, specially designed for bonded semi conductive screen applications. Applications: LE0592 is intended for semi conductive applications in XLPE m..
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D 638
Cossa Polimeri ESTASTIR HI 0408 V0 Flame Retardant Polystyrene Flame retardant class V0, PBDE free, good impact resistance, good thermal resistance, high light resistance, good processabilityInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527-1/-2
Covestro Desmopan® DP 1960AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Tensile Strength at Break	22.0 MPa	3190 psi
Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good low-temperature and elasticity characteristics.Information provided by Daikin Industries.
Tensile Strength at Break	22.0 MPa	3190 psi
Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance, good mold flow.Information provided by Daikin Industries.
Tensile Strength at Break	22.0 MPa	3190 psi	50 mm/min; ISO 527
Chi Mei Polyrex® PH-88 Polystyrene - High Impact High impact
Tensile Strength at Break	>= 22.0 MPa	>= 3190 psi	ISO R 527
Fainplast Compounds FKT 0296/1 Flexible PVC, Insulation Lead Free General purposes
Tensile Strength at Break	22.0 MPa	3190 psi	50 mm/min; ISO 527
Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin Starpylen MB006SU is a Glass Bead Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® SC948 NC010 Polyester Elastomer TPC-ET (Unverified Data**) 40 Shore D High Performance Polyester Elastomer Developed for the Healthcare Industry Hytrel SC948 NC010 is a low modulus grade with nom. durometer hardness of 40D contains non-discoloring stabilize..
Tensile Strength at Break	22.0 MPa	3190 psi	ISO R 527
Fainplast Compounds PH 90/AS Flexible PVC, Transparent Extrusion Food belt carriers
Tensile Strength at Break	22.0 MPa	3190 psi	ISO R 527
Addiplast Addilene H 555 Y7 Polypropylene Homopolymer Good surface appearance, high temperature resistanceInformation provided by Addiplast.
Tensile Strength at Break	22.0 MPa	3190 psi	ISO 527-2
Arkema Group OREVAC® CA 100 Grafted Maleic Anhydride Polypropylene OREVAC® CA 100 is a chemically functionalized polypropylene with a high content of maleic anhydride. Grafting on polypropylene backbone is achieved with a processing technology which allows to opti..
Tensile Strength at Break	22.0 MPa	3190 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436G5M25CL Glass/Mineral Reinforced Coupled
Tensile Strength at Break	>= 22.0 MPa	>= 3190 psi	ASTM D4745-11
Adamas Adalon® 816 PTFE, 46% Bronze, Blue Information provided by Adamas, HPM
Tensile Strength at Break	22.0 MPa	3190 psi	50mm/min; ASTM D638
3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride (discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesInformation provided by Dyneon, A 3M..