Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Melt Flow 2.0 - 6.0 g/10 min
2.0 - 6.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Tensile Strength, Yield 72.4 MPa
10500 psi
ASTM D638
Flexural Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 3.45 GPa
500 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 127 °C
260 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Flammability, UL94 HB
HB
1/16 in
HB
HB
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 304 °C
500 - 580 °F
Middle Barrel Temperature 271 - 310 °C
520 - 590 °F
Front Barrel Temperature 282 - 316 °C
540 - 600 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 71.1 - 104 °C
160 - 220 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour