SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact, Wear Resistant.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM D792
1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.700 %
0.700 %
50% RH, 24 hrs; ASTM D570
1.12 %
1.12 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.024 - 0.026 cm/cm

@Time 86400 sec
0.024 - 0.026 in/in

@Time 24.0 hour
ASTM D955
0.0243 - 0.026 cm/cm

@Time 86400 sec
0.0243 - 0.026 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.024 - 0.026 cm/cm

@Time 86400 sec
0.024 - 0.026 in/in

@Time 24.0 hour
ASTM D955
0.0243 - 0.026 cm/cm

@Time 86400 sec
0.0243 - 0.026 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ASTM D638
54.0 MPa
7830 psi
ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527
59.0 MPa
8560 psi
ASTM D638
Elongation at Break 31 %
31 %
ASTM D638
64 %
64 %
ISO 527
Elongation at Yield 8.0 %
8.0 %
ASTM D638
16 %
16 %
ISO 527
Tensile Modulus 2.16 GPa
313 ksi
1 mm/min; ISO 527
2.22 GPa
322 ksi
50 mm/min; ASTM D638
Flexural Strength 74.0 MPa
10700 psi
ISO 178
80.0 MPa
11600 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
2.08 GPa
302 ksi
ASTM D790
Izod Impact, Notched 4.27 J/cm
8.00 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 19.0 kJ/m²
9.04 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 76.0 J
56.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 65.0 J
47.9 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.31
0.31
ASTM D3702 Modified
Coefficient of Friction, Static 0.18
0.18
ASTM D3702 Modified
K (wear) Factor 16.1 x 10-8 mm³/N-M
8.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 121 µm/m-°C

@Temperature -40.0 - 40.0 °C
67.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
121 µm/m-°C

@Temperature -40.0 - 40.0 °C
67.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 112 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
113 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 188 °C
370 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
206 °C

@Thickness 3.20 mm
403 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 67.0 °C
153 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
unannealed; ASTM D648