Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade
| Category | Polymer , Thermoplastic , Polyketone , PEKK, Unreinforced |
| Manufacturer | Performance Polymers |
| Trade Name | IPS II |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amber pellets; neat resinInformation provided by Infinite Polymer System II.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 40 g/10 min @Load 8.40 kg, Temperature 360 °C |
40 g/10 min @Load 18.5 lb, Temperature 680 °F |
|
| Crystallinity | 0.00 % | 0.00 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 86 | 86 | ASTM D785 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Modulus of Elasticity | 3.40 GPa | 493 ksi | ASTM D638 |
| Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Compressive Yield Strength | 103 MPa | 14900 psi | ASTM D695 |
| Poissons Ratio | 0.45 | 0.45 | |
| Shear Modulus | 1.17 GPa | 170 ksi | Calculated |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.17 mm |
0.937 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Gardner Impact | >= 36.2 J | >= 26.7 ft-lb | |
| Coefficient of Friction | 0.186 | 0.186 | ASTM D1894 |
| Coefficient of Friction, Static | 0.285 | 0.285 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 77.0 µm/m-°C | 42.8 µin/in-°F | Below glass transition temp; ASTM D696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 306 °C | 583 °F | DSC |
| Maximum Service Temperature, Air | 250 °C | 482 °F | UL Continuous Use Temp. |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| Glass Transition Temp, Tg | 155 °C | 311 °F | DSC |
| Flammability, UL94 | V-0 | V-0 | |
| NBS Smoke Density | <= 10 | <= 10 | |
| Oxygen Index | 40 % | 40 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz |
3.3 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 23.6 kV/mm | 599 kV/in | ASTM D149 |
| Dissipation Factor | 0.0040 @Frequency 1000 Hz |
0.0040 @Frequency 1000 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- MV Labs CS700 CsNO3 Cesium nitrate
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 52A
- Westlake Epolene® C-26 Coating Grade - Highly Branched Medium Molecular Weight Polyethylene Polymer, Maleation Processed
- Eagle Brass 301 Austenitic Stainless Steel, 3/4 Hardened
- ConocoPhillips 680 Gear Oil AGMA Lubricant No. 8EP
- Aclo Accutech Polypropylene Homopolymer HP0339C20L Calcium Reinforced
- Ascend Performance Materials Vydyne® 21SPC1 Nylon 66, DAM
- BASF Ultramid® A27 E 01 PA66 (Conditioned)
- Materion PROtherm® Beryllium Copper Alloy
Copyright © lookpolymers.com All Rights Reserved