Polymer Property : Linear Mold Shrinkage, Flow = 0.024 in/in Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopoly (Asia Pacific) LNP* Lubricomp* KP003AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopoly (Asia Pacific) LNP* Lubricomp* KP003AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer LNP* LUBRICOMP* KP003AXZ is a compound based on Acetal Homopolymer resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer LNP* LUBRICOMP* KP003AXZ is a compound based on Acetal Homopolymer resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.024 - 0.026 cm/cm @Time 86400 sec	0.024 - 0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66 LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact, Wear Resistant.
Linear Mold Shrinkage, Flow	0.024 - 0.026 cm/cm @Time 86400 sec	0.024 - 0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66 (Asia Pacific) LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.024 - 0.026 cm/cm @Time 86400 sec	0.024 - 0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.024 - 0.026 cm/cm @Time 86400 sec	0.024 - 0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific) LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.024 - 0.026 cm/cm @Time 86400 sec	0.024 - 0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KB003RXZ Acetal Copolymer LNP THERMOCOMP* KB003RXZ is a compound based on Acetal Copolymer resin containing 15% Glass Bead. Added features of this material include: Easy Release.
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.