SABIC Innovative Plastics LNP LUBRICOMP FL004 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP FL004 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing 20% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 6.00 MPa | 870 psi | 5 mm/min; ISO 527 |
| 12.0 MPa | 1740 psi | Type I, 5 mm/min; ASTM D638 | |
| 25.0 MPa | 3630 psi | ASTM D638 | |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | Type I, 5 mm/min; ASTM D638 |
| 23.0 MPa | 3340 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 42 % | 42 % | ASTM D638 |
| 78 % | 78 % | 5 mm/min; ISO 527 | |
| 148 % | 148 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 7.9 % | 7.9 % | 5 mm/min; ISO 527 |
| 8.2 % | 8.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.00 GPa | 145 ksi | 1 mm/min; ISO 527 |
| 1.24 GPa | 180 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 19.0 MPa | 2760 psi | ISO 178 |
| 20.0 MPa | 2900 psi | ASTM D790 | |
| Flexural Modulus | 0.930 GPa | 135 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.930 GPa | 135 ksi | 2 mm/min; ISO 178 | |
| 1.00 GPa | 145 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² | 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.11 | 0.11 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 137 µm/m-°C @Temperature -30.0 - 30.0 °C |
76.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 121 µm/m-°C @Temperature -30.0 - 30.0 °C |
67.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm |
127 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Materion BrushCAST® 20CT Fine Grain Casting Alloy (Solution Annealed & Aged)
- Menzolit Menzolit® SMC 0412 Unsaturated Polyester UP
- Solvay Technyl® C 218 V50 50% Glass Filled, Heat Stabilized Nylon 6
- Dow Corning ES-5612 Silicone Formulation Aid
- Akro-Plastic Akromid® B3 GF 50 RM-M (3146) PA 6 Conditioned, 50% Glass Filled
- Asia International Enterprise (Hong Kong) 60C2 Nylon 66
- Poco Graphite Glassmate® SR Graphite
Copyright © lookpolymers.com All Rights Reserved