SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.940 % | 0.940 % | 50% RH, 24 hrs; ASTM D570 |
| 1.60 % | 1.60 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
| 102 MPa | 14800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.97 GPa | 721 ksi | 5 mm/min; ASTM D638 |
| 5.08 GPa | 737 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 153 MPa | 22200 psi | ISO 178 |
| 158 MPa | 22900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 4.29 GPa | 622 ksi | 2 mm/min; ISO 178 |
| 4.62 GPa | 670 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.0300 J/cm | 0.0562 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.45 J/cm | 6.46 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 239 °C @Thickness 3.20 mm |
462 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled
- SABIC PS 325 High Impact Polystyrene for Injection Molding
- PolyOne Edgetek® X AS-40CF/000 Natural SE Acrylonitrile Butadiene Styrene (ABS)
- MetalTek MTEK CZ-100 Cast UNS N02100 Severe Corrosion and Heat Resistant Alloy
- Lord Adhesives 660 White, Non Sag, Fast Set for FRP Acrylic Adhesive
- Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded
- Master Bond EP21TDC-7 Highly Flexible Two Component Epoxy System
- DuPont Performance Polymers Neoprene WD Polychloroprene Rubber
- AdvanSource Biomaterials ChronoThane™ P Thermoplastic Polyurethane Elastomer
- 3M Scotchcal™ 50-27 Graphic Film
Copyright © lookpolymers.com All Rights Reserved